Chemical and Material Engineering Essay Example | Topics and Well Written Essays - 1000 words

Chemical and Material Engineering - Essay Example The process of analyzing the mechanical qualities of nc by researchers is gradual since this process is experiencing various obstacles. Manufacture of the nc materials is one of the Chief impediments of the experimental evaluations of its properties. The preparation of nc involves factors, for example, porosity, contamination and residual stress, which significantly influence its mechanical capabilities (Lu, Lu & Sui, 4127). Indeed, a valid evaluation of the mechanical qualities of the nc requires a sample that is deficient of the contamination and residual stress. Such a sample will have to be large to ensure several tests are done on it. A significant quantity of nc pure copper was synthesized through an electrodeposition technique. Copper (Cu) metal has unique characteristics that make it suitable for in manufacturing the nc sample. Cu has an extensibility quality when undergoing cold rolling at average room temperature (Lu, Lu & Sui, 4127). The deformation feature of Cu has been researched at length through high-resolution electron microscopy (HRTEM). Experimental Procedures According to (Lu, Lu & Sui, 4128), the manufacture of nc copper entails the electrodeposition process through an electrolyte of CuSO4. This is a chemical procedure where the substrate of Cu is deposited on the cathode, which has a capacity of 99.99wt%. The electrolyte had an acidity of 0.9 mol/l and the solution temperature was a moderate 20Â ±1. The purity of the deposits of nc Cu was better than that of 99.993 at% (exclusive of oxygen). If the oxygen content were inclusive, the nc Cu sample would be at 99.98 at%. The Archimedes principle was the standard that researchers were utilizing to measure the density of the nc Cu sample (Lu, Lu & Sui, 4128). The density of the sample was 8.91?0.03 g/cm3, which is indifferent from that of pure Cu, which is 8.96 g/cm3. X-ray diffraction and HRTEM analysis were essential in determining thee microstructure of the Cu sample. The determination of t he nc Cu samples thermal characteristics was through differential scanning calorimetry (DSC). Plastic deformation of Cu was through cold rolling, which resulted in its extension in length. Results and Discussion The X-ray diffraction was displaying a Cu sample that was exhibiting {110} texture. This sample was showing a substantial broadening of a mean of 28 nm grain size and 0.14% of microstain. This was at a degree of deformation of 2300% (Lu, Lu & Sui, 4128). However, after the cold rolling process the microstain levels in the sample increase but the grain size remains constant at 28nm. Coldrolling of a coarse-grained Cu in similar conditions was producing different results. The microstain level did increase by 0.04% to 18% while the sample disintegrated to a degree of deformation of 800%. Thermal analysis The evaluation of the thermal characteristics was of a temperature bracket of 50Â °C to 250Â °C at a constant combustion of 5Â °C/min (Lu, Lu & Sui, 4130). The implications of these processes were subject to a DSC scan, which was showing no oxidation of the nc Cu samples. There was annealing of nc Cu at various temperature and afterwards cooled by the DSC process. Increment of the grain size of nc Cu from 75Â °C to 200Â °C was evident by 50 nm. Grain boundary enthalpy XRD results were representative of the grain growth of nc CU from 30nm to 80nm. Essentially, grain boundary enthalpy entails two procedures (Lu, Lu & Sui, 4132). The first is the dislocation of grain boundaries, which